were replaced by a 56lb. with the intention of adding small weights when suspended; the whole was then raised so imperceptibly by the screw, that the only way of ascertaining that it was suspended, was by looking under the scale to see that it was clear of the rest. As soon as it was half-an-inch clear it snapped, thus breaking at once with one pound less than it resisted for nearly two minutes.
"Six experiments were carefully conducted at 60�� F., the parts of the bars being selected so as to give to each set of experiments similar portions of both bars; the results are marked on the pieces. My assistant now prepared a refrigerating mixture which stood at zero, the bars were immersed for some time in this, and we prepared for the breaking trials to be made as quickly as could be, consistently with accuracy; and to secure the low temperature, each bar, on being placed in the machine, had its surface at top covered with the freezing mixture. The bars at zero broke with more regularity than at 60��, but instead of the results confirming the general impression as to cold rendering iron more brittle, they are calculated to substantiate an exactly opposite idea, namely, that reduction of temperature, c?teris paribus, increases the strength of cast iron. The only doubtful experiment of the whole twelve is the first, and as it stands much the highest, the probability is that it should be lower; yet, even taking it as it stands, the average of the six experiments at 60�� F., gives 4cwt. 4lb. as the breaking weight of the bar at that temperature, while the average of the six experiments at zero gives 4cwt 20lb. as the breaking weight of the bar at zero, being an increase of strength, from the reduction of temperature, equal to 3.5 per cent."
Sir W. Fairbairn states: "It has been asserted, in evidence given at the coroner's inquest, in a recent railway accident, that the breaking of the steel tire was occasioned by the intensity of the frost, which is supposed to have rendered the metal, of which this particular tire was composed, brittle. This is the opinion of most persons, but judging from my own experience such is not the fact. Some years since I endeavored to settle this question by a long and careful series of experiments on wrought iron, from which it was proved that the resistance to a tensile chain was as great at the temperature of zero as it was at 60�� or upwards, until it attained a scarcely visible red heat."
The immense number of purposes to which both iron and steel are applied, and the changes of temperature to which they are exposed, renders the inquiry not only interesting in a scientific point of view, but absolutely necessary to a knowledge of their security under the various influences of those changes. It was for these reasons that the experiments in question were undertaken, and the summary of results is sufficiently conclusive to show that changes of temperature are not always the cause of failure. Sir W. Fairbairn adds: "The danger arising from broken tires does not, according to my opinion, arise so much from changes of temperature as from the practice of heating them to a dull red heat, and shrinking them on to the rim of the wheels. This, I believe, is the general practice, and the unequal, and in some cases, the severe strains to which they are subject, has a direct tendency to break the tires."
* * * * *

OAK GRAINING IN OIL COLORS.
CONDENSED FROM THE BUILDING NEWS.
There is a charm and feeling about work executed by the hand, which gives it a value no mere machine work can possess. Machine work, from its very nature, necessitates a repetition of pattern, which cannot be avoided. Hand-work, on the contrary, can imitate every variety, and follow nature so closely that no two pieces need be alike. There is also in hand-work a wide scope for the inventive faculty and the exercise of good taste (both in form and color) and skillful workmanship. As a rule, strong contrasts between the ground and the graining color should be avoided. The figure and grain should of course be seen clearly, but only so clearly as to be distinct, without interfering with the general and uniform quietness of tone necessary to fulfil the conditions required by the laws of harmony and good taste. Violent contrasts and gaudy coloring are always vulgar, brilliancy and richness of color are not necessarily vulgar; it is the absence of the guiding power of knowledge and pure taste in their arrangement which degrades them to the rank of vulgarity. We have before spoken of the importance of good combing, and of the various kinds of